ATORN twist drill HSSE-V3 TiAlN 3XD 4.1 x 6 mm x 55 mm
Brand: ATORN
Surface: TiAlN
Length: 55 mm
DIN: 1897
Art.-no. 11036241
Manufacturer article no. 12280373
EAN 4050293451009
Individual prices for customers after login
Application
Universal use in all material groups up to a strength of 1300 N/mm²
Execution
- Twist drill with unified shaft
- Diameter 1.00 mm–1.90 mm = tip angle 140°
- Diameter 2.00 mm–4.00 mm = tip angle 130°
- Diameter 4.10 mm–20.0 mm = tip angle 120°
- 2 drill heels
- 38° to 40° spiral angle
- Straight main cutting edge
Advantage
- Drilling without centring
- Problem solver in low-performance machines without internal cooling in high-strength steels and stainless steels
- Extremely hard, low-friction and temperature-resistant TiAlN coating for longer life
- Very high feed rates can be achieved
Brand | ATORN |
Main EAN Code | 4050293451009 |
Manufacturer Part Number | 12280373 |
Cutting material | HSSE V3 |
Surface | TiAlN |
Type | VA |
Self-centring | Yes |
Tool holding device | HA parallel shank |
Cutting edge diameter | 4.10 mm |
Angle of the tip | 120 Degree |
Chip flute length | 22 mm |
Length | 55 mm |
f steel 1000 | 0.14 mm/r |
DIN | 1897 |
Gross Weight | 0.008 kg |
| Material groups for cutting values | Description regarding DIN | Strength Class [N/mm²] | Material No. | Vc [m/min] | f [mm/r] with diameter | Suitability |
|---|---|---|---|---|---|---|
| 1.00 Steels | ||||||
| 1.01 Free machining steel | 9 S 20 | < 900 | 1.0711 | 50-60 | 0.13-0.18 | ⚫ |
| 1.02 Structural steel | ST 37-2 | <500 | 1.0037 | 50-60 | 0.13-0.18 | ⚫ |
| 1.03 Structural steel | ST 60-2 | > 500 | 1.7735 | 40-55 | 0.13-0.18 | ⚫ |
| 1.04 Heat-treated steel | 42 CrMo 4 | <1000 | 1.7225 | 20-35 | 0.13-0.18 | ⚫ |
| 1.05 Cast iron | GS-45 | <1000 | 1.0446 | 18-26 | 0.13-0.18 | ⚫ |
| 1.06 Case-hardened steel | 16 MnCr 5 | <1200 | 1.7131 | 18-22 | 0.13-0.18 | ⚫ |
| 1.07 Ferritic/martensitic stainless steel | X 10 Cr 13 | <1100 | 1.4006 | 15-20 | 0.06-0.1 | ⚫ |
| 1.08 Heat-treated steel | 43 CrMo 4 | >1000 | 1.3563 | 18-24 | 0.13-0.18 | ⚫ |
| 1.09 Nitriding steel | 31 CrMoV 9 | <1300 | 1.8519 | 18-22 | 0.13-0.18 | ⚫ |
| 1.10 Tool steel | X 38 CrMoV 5 1 | <1300 | 1.2343 | 18-22 | 0.13-0.18 | ⚫ |
| 2.00 Stainless steels | ||||||
| 2.01 Austenitic stainless steel | G-X 2 CrNiMo 18 15 | <1100 | 1.3953 | 13-18 | 0.06-0.1 | ⚫ |
| 3.00 Non-ferrous metals | ||||||
| 3.01 Long-chipping aluminium | AI99.9 | <500 | 3.0305 | 60-100 | 0.18-0.3 | ⚫ |
| 3.02 Short-chipping aluminium | G-AISi12 | <500 | 3.2581 | 30-60 | 0.18-0.3 | ⚫ |
| 3.03 Copper alloy bronze, long-chipping | CuSn4 | <1200 | 2.1016 | 50-60 | 0.13-0.18 | ⚫ |
| 3.04 Copper alloy bronze, short-chipping | CuNi12Zn24 | <850 | 2.0730 | 20-45 | 0.13-0.18 | ⚫ |
| 3.05 Copper alloy brass, long-chipping | Cu Zn 20 | <600 | 2.0250 | 20-35 | 0.18-0.3 | ⚫ |
| 3.07 Thermoplastic | Cu Zn 39 Pb 3 | <600 | 2.0381 | 30-60 | 0.18-0.3 | ⚫ |
| 3.07 Thermoplastic | PVC, Acrylglas | <100 | - | - | ⚫ | |
| 3.08 Duroplast | Bakelit, Melamin | <150 | - | - | ⚫ | |
| 3.09 Fibre-reinforced plastics | CFK, GFK | <1500 | - | - | ||
| 3.10 Graphite | C8000 | <60 | - | - | ||
| 3.11 Composite materials | - | - | ||||
| 4.00 Cast metal | ||||||
| 4.01 Grey cast iron | GG10 | <260 HB | 0.6010 | 25-50 | 0.16-0.22 | ⚫ |
| 4.02 Spheroidal graphite iron | GGG 40 | <310 HB | 0.7040 | 32-40 | 0.16-0.22 | ⚫ |
| 4.03 Ductile iron | GTW-55 | <280 HB | 0.8055 | 32-40 | 0.16-0.22 | ⚫ |
Last viewed
SUBITO coated centring plate for 12.0-20 mm measuring range
ATORN screwdriver TX-IP/TX-Plus 6
ATORN wire cup brush 60 mm diameter, M14 crimped steel wire 0.3 mm
Shim for indexable inserts VNM.1604.. (3717)
DAkkS calibration depth callipers 0–600 mm
Packing foam thickness 2 mm WxL 1250 mmx250 m colour: white, roll
ATORN hand tap MS HSSE D 352 0° M2.5 0.45 mm ISO2 D/S 3xD VA
ORION high-perf. drill, SC TiAlN, HPC 8xD 4.7 mm x 6 mm x 95 mm HB internal
HOFE shelving rack basic bay 1,000x600 mm, 5 zp. shelves, 330 kg HZG20610XS