ORION end mill HSSE8-TICN, 25.0 mm, HR, long, shank DIN 1835B T=5
Brand: ORION
Surface: TiCN
Length: 166 mm
Art.-no. 15300250
Manufacturer article no. 15300250
EAN 4039247095025
Individual prices for customers after login
Application
End mill for universal use when plunge milling, groove milling and keyway cutting as well as face milling and peripheral milling.
Execution
- HSSE Co 8
- fine roughing teeth
- centre cutting (over diameter 20 mm without centre cutting)
- TiCN coating for long service life
- straight shank in accordance with DIN 1835 B
Brand | ORION |
Main EAN Code | 4039247095025 |
Manufacturer Part Number | 15300250 |
Cutting material | HSSE Co8 |
Surface | TiCN |
Type | HR |
Number of cutting edges (Z) | 5 PCS |
Twist angle | 30° |
Edge protection chamfer length | 0.2 mm |
Tool holding device | HB parallel shank |
Construction length | Long |
Cutting edge diameter | 25 mm |
Cutting edge length | 90 mm |
Length | 166 mm |
Shank diameter | 25 mm |
fz steel 1300 | 0.12 mm |
Gross Weight | 0.542 kg |
Material groups for cutting values | Description regarding DIN | Strength Class [N/mm²] | Material No. | Vc [m/min] | fz [mm/T] at diameter | Suitability |
---|---|---|---|---|---|---|
1.00 Steels | ||||||
1.01 Free machining steel | 9 S 20 | < 900 | 1.0711 | 40-45 | 0.09-0.1 | ⚪ |
1.02 Structural steel | ST 37-2 | <500 | 1.0037 | 40-45 | 0.09-0.1 | ⚪ |
1.03 Structural steel | ST 60-2 | > 500 | 1.7735 | 32-36 | 0.08-0.09 | ⚪ |
1.04 Heat-treated steel | 42 CrMo 4 | <1000 | 1.7225 | 32-36 | 0.08-0.09 | ⚪ |
1.05 Cast iron | GS-45 | <1000 | 1.0446 | 20-25 | 0.08-0.09 | ⚪ |
1.06 Case-hardened steel | 16 MnCr 5 | <1200 | 1.7131 | 35-45 | 0.08-0.09 | ⚪ |
1.07 Ferritic/martensitic stainless steel | X 10 Cr 13 | <1100 | 1.4006 | 18-20 | 0.08-0.09 | ⚫ |
1.08 Heat-treated steel | 43 CrMo 4 | >1000 | 1.3563 | 20-25 | 0.08-0.09 | ⚫ |
1.09 Nitriding steel | 31 CrMoV 9 | <1300 | 1.8519 | 14-16 | 0.08-0.09 | ⚫ |
1.10 Tool steel | X 38 CrMoV 5 1 | <1300 | 1.2343 | 14-16 | 0.08-0.09 | ⚫ |
2.00 Stainless steels | ||||||
2.01 Austenitic stainless steel | G-X 2 CrNiMo 18 15 | <1100 | 1.3953 | 20-28 | 0.08-0.09 | ⚪ |
3.00 Non-ferrous metals | ||||||
3.01 Long-chipping aluminium | AI99.9 | <500 | 3.0305 | 180-350 | 0.08-0.09 | |
3.02 Short-chipping aluminium | G-AISi12 | <500 | 3.2581 | 80-90 | 0.08-0.09 | ⚪ |
3.03 Copper alloy bronze, long-chipping | CuSn4 | <1200 | 2.1016 | 30-40 | 0.08-0.09 | |
3.04 Copper alloy bronze, short-chipping | CuNi12Zn24 | <850 | 2.0730 | 40-50 | 0.08-0.09 | ⚪ |
3.05 Copper alloy brass, long-chipping | Cu Zn 20 | <600 | 2.0250 | 40-45 | 0.08-0.09 | |
3.07 Thermoplastic | Cu Zn 39 Pb 3 | <600 | 2.0381 | 45-55 | 0.08-0.09 | ⚪ |
3.07 Thermoplastic | PVC, Acrylglas | <100 | 120-150 | 0.08-0.09 | ||
3.08 Duroplast | Bakelit, Melamin | <150 | 80-90 | 0.08-0.09 | ||
3.09 Fibre-reinforced plastics | CFK, GFK | <1500 | 80-90 | 0.08-0.09 | ||
3.10 Graphite | C8000 | <60 | - | - | ||
3.11 Composite materials | - | - | ||||
4.00 Cast metal | ||||||
4.01 Grey cast iron | GG10 | <260 HB | 0.6010 | 30-50 | 0.1-0.12 | ⚪ |
4.02 Spheroidal graphite iron | GGG 40 | <310 HB | 0.7040 | 30-50 | 0.1-0.12 | ⚪ |
4.03 Ductile iron | GTW-55 | <280 HB | 0.8055 | 30-50 | 0.1-0.12 | ⚪ |
5.00 Special alloys | ||||||
5.01 Titanium alloy | TiAI5Sn2,5 | <1200 | 3.7115 | 10-20 | 0.08-0.09 | ⚪ |
5.02 Nickel-based alloy | NiCr21Mo | <1400 | 2.4858 | 10-20 | 0.08-0.09 | ⚫ |
5.03 Super alloys | X45CrSi 9 3 | <1400 | 1.4718 | 10-20 | 0.08-0.09 | ⚫ |